Glass Filled PEEK

JUTAIPEEK^?GF30 is a type of Polymeric Profiles made from 30% of short-cut Glass Fiber Reinforced Polyetherether Ketone (PEEK). (JUTAIPEEK^?GF30V is an extruded profile using VICTREX PEEK Polymers 450GL30 raw materials, and JUTAIPEEK^?GF30G is an extruded profile using domestic raw materials). Compared to PEEK of no-reinforcement, the HDT increases obviously, the strength and modulus increase a certain extent, and it has better wear-resistance and lower thermal expansion.
This type of products can be applied in the operating condition that is need to bear larger mechanical stress and wear rate in higher temperature, such as semiconductor production process, precision bearing, tubes and components in chemical equipment and electrical system.

Product Features

JUTAIPEEK^?GF30 type Glass Fiber Reinforced PEEK profiles:
● Good tensile performance, and Tensile Modulus=5-7GPa.
● Good flexural performance, and Flexural Modulus≥6GPa.
● Outstanding thermal mechanical bearing capacity, and HDT≥250℃.
● Outstanding wear-resistance.
● Outstanding electrical insulation, and dielectric performance.
● Excellent dimensional stability and low thermal expansion.
● High thermal endurance and the long service temperature is 250℃.

Application Fields

JUTAIPEEK^?GF30 type Glass Fiber Reinforced PEEK profiles can be applied:
—— Mechanical Engineering Industry；
—— Electrical Industry；
—— Semiconductor and Electronic Industry；
—— Chemical Industry and Petrochemical Industry.

Instructions for Use

Machined by Lathes or Milling Machine.

Remove surface heat-treatment aged layers and the thickness of removal layer is 0.5-1mm.

Product Storage Instructions

Placed away from light, avoiding humid, and away from oily substance.
Packed with polymeric film when not use.

Product Technical Data

The performance of JUTAIPEEK^?GF30 series products is as follows:

Performance	Test Method	Unit	GF30G	GF30V
Color	Eye	/	Grey-Yellow	Grey-Yellow
Density	ISO 1183-1	g/cm3	1.52	1.52
Tensile Strength	ISO 527-2	MPa	≥105	≥110
Tensile Modulus	ISO 527-2	GPa	≥6	≥6
Elongation At Break	ISO 527-2	%	≥8	≥8
Charpy Impact Strength	ISO 179	KJ/m2	≥4.0	≥5.0
Flexural Strength	ISO 178	MPa	≥200	≥205
Flexural Modulus	ISO 178	GPa	≥7	≥6.5
Rockwell Hardness	ISO 2039-2	HRM	≥100	≥100
Thermal Conductivity	ISO 8302	W/ (m?K)	0.35	0.35
Coefficient of Linear Thermal Expansion 20-100℃	ISO 11359-2	10^-6/K	≤30	≤30
Long Service Temperature	UL 746B	℃	250	250
Heat Deflection Temperature	ISO 75-2	℃	≥250	≥250
Water Absorption （24h）	ISO 62	%	≤0.1	≤0.1
Flame Retardancy	UL 94	/	V-0	V-0
Volume Resistivity	IEC 61340-2-3	Ω?cm	10¹¹-10¹³	10¹¹-10¹³