JUTAIPEEK^?NA type pure PEEK profiles:
● Outstanding stiffness and mechanical strength.
● Excellent resistance to creep and fatigue.
● Maintaining higher tensile strength and flexure strength、 above 200℃.
● Outstanding heat-resistance with long term service temperature is 240-260℃.
● Outstanding electrical insulation， low dielectric constant and dielectric loss.
● Outstanding resistance to chemicals.
● Excellent resistance to hot water and steam， which can be serviced long term in steam with temperature above 200℃.
● Excellent flame retardancy， which reach UL94 V-0 class for 1.6mm thickness sample.
● Low smoke generation.
● Outstanding resistance to nuclear radiation， which has the best radiation-resistance in Polymeric materials.
● Good sliding frictional property， which has better friction factor and wear rate than most of other kinds of polymeric polymers.

JUTAIPEEK^?NA type PEEK profiles can be applied:
—— Mechanical Engineering Industry；
—— Pump and Vale Industry；
—— Electronic Industry；
—— Chemical Industry；
—— New Energy Industry；
—— Food and Medical Device Industry；
—— Automobile Industry；
—— Aviation and Aerospace industry.

Machined by Lathes or Milling Machine. Remove surface.
heat-treatment aged layers and the thickness of removal layer is 0.5-1mm.

Placed away from light, avoiding humid, and away from oily substance.
Packed with polymeric film when not use.

The performance of JUTAIPEEK^?NA series products is as follows:

Performance	Test Method	Unit	NAG	NAV
Color	Eye	/	Rice-Yellow	Rice-Yellow
Density	ISO 1183-1	g/cm3	1.30	1.30
Tensile Strength	ISO 527-2	MPa	≥105	≥105
Tensile Modulus	ISO 527-2	GPa	≥4.0	≥4.0
Elongation At Break	ISO 527-2	%	≥15	≥25
Notched Charpy Impact Strength	ISO 179	KJ/m2	≥5.6	≥4.5
Flexural Strength	ISO 178	MPa	≥160	≥165
Flexural Modulus	ISO 178	GPa	≥4.0	≥4.0
Rockwell Hardness	ISO 2039-2	HRM	≥100	≥100
Thermal Conductivity	ISO 8302	W/ (m?K)	≤0.5	≤0.5
Coefficient of Linear Thermal Expansion 20-100℃	ISO 11359-2	10-6/K	≤65	≤65
Long Service Temperature	UL 746B	℃	240	240
Heat Deflection Temperature	ISO 75-2	℃	≥150	≥150
Water Absorption (23℃、Water、24h)	ISO 62	%	≤0.05	≤0.05
Flame Retardancy	UL 94	/	V-0	V-0
Volume Resistivity	IEC 62631-3-1	Ω?cm	1011-1013	1011-1013
Dielectric Strength	IEC 60243-1	kV/mm	≥15	≥15
Dielectric Constant	IEC 60243-1	1	3.66	3.3
Dielectric Loss	IEC 60243-1	1	2.5*10-3	2.7*10-3

JUTAIPEEK^?NA can maintain excellent chemical tolerance and mechanical property under considerably wide temperature range, with generally seldom expansion or color fade. The chemical corrosion resistance of JUTAIPEEK^?NA is demonstrated in Table 5.

50%Acetamide, Formamide and Other Amide	+	40% HF	-
Acetone, Cyclohexanone, MEK and Other Ketones	+	Liquid Freon	-
10%Ammonia, Cyclohexamine and Other Amines.	+	Urea Solution	+
Gasoline, Diesel, Fuel, Asphalt	+	Lipiodol	0
Benzene, Toluene and Other Aromatic hydrocarbons	+	Potassium hydroxide solution	+
Acids such as 10% Acetic acid, 10% Formic acid,Concentrated phosphoric acid, 10% Nitric acid, 10% Hydrochloric acid, 10% Sulfuric acid, etc.	+	1% potassium permanganate	+
		Dichloromethane	+
10% Calcium chloride, 10% Calcium carbonate, 10%Sodium nitrate, 10% Sodium thiosulfate and Other Salts 10% Hydrochloric acid, 10% Sulfuric acid, etc.	+	Nitrobenzene	0
		Phenol solution	0
96% Ethanol, Ethylene glycol, Glycerol, 40% Ethylene glycol solution, Methanol, Propanol and Other Alcohols	+	Pyridine	+
		Salicylic acid	-
Hexane, Heptane, Octane, Isopropane and Other Alkanes	+	SO2	+
30% Formaldehyde solution and other Aldehydes	+	98% carbonate solution	-
10% Boric acid aqueous solution	+	Saturated hydrogen sulfide solution	+
Chlorobenzene	0	Silicone oil	+
Chloroform	+	Styrene	+
Dichloro heterocyclic hexane	+	CCl4	+
Concentrated acetic acid	0	THF	+
Diethyl ether	+	TEOA	0

Plastic combustion generates a series of toxic gases, such as hydrogen cyanide (HCN), sulfur gases (SO₂, H₂S), nitrogen gases (NO, NO₂) and carbon monoxide (CO). These gases are more lethal than fire because they can render people incapable of escaping from the fire scene. Corrosive gases such as hydrogen fluoride (HF) and hydrogen chloride (HCl) can cause permanent damage to sensitive electronic devices.
The combustion products of JUTAIPEEK are mainly carbon dioxide (CO₂) and carbon monoxide (CO). The amount of carbon monoxide produced is even less than 5% of the limit value specified in the Aviation Toxicity Standards (e.g. Boeing BSS 7238 and Airbus ATS-1000).

The toxicity of gases is usually measured based on the amount of gases that cause fatal damage to the human body. Table 2 is the test results of the National Bureau of Standards (NBS) Smoke Laboratory, which confirms that the only toxic gas produced considerably is carbon monoxide（CO).

Table below: The National Bureau of Standards (NBS) smoke laboratory tests the toxicity of combustion gases

	Flameless test [ppm]		Flame test [ppm]		Max allowable concentration [ppm]
	After 90s	After 4Mins	After 90s	After 4Mins	After 90s	After 4Mins
CO	Smallest	1	30	100	3000	3500
HCI	0	0	0	0	50	500
HCN	0	0	0	0	100	150
H2S,SO2	0	0	0	0	50	100
NOx	0	0	0	0	50	100
HF	0	0	0	0	50	50